Nafion™ Membrane is used to separate the anode and cathode compartment of Proton Exchange Membrane fuel cells and water electrolyzers. The thickness of this particular membrane, Nafion™ 211 makes it suitable for many Hydrogen Air/Oxygen Fuel Cell applications. Nafion™ 211 is 25.4 micrometers (1 mil) thick. The membrane is positioned between a backing film and a coversheet.
Chemours' Nafion™ PFSA NR-211 membranes are based on chemically stabilized perfluorosulfonic acid/PTFE copolymer in the acid (H+) form, and exhibit substantially lower fluoride ion release compared to the non-stabilized polymer – a sign of improved chemical durability. Nafion™ PFSA membranes are widely used for Proton Exchange Membrane (PEM) fuel cells and water electrolyzers. The membrane performs as a separator and solid electrolyte in a variety of electrochemical cells that require the membrane to selectively transport cations across the cell junction. The polymer is chemically resistant and durable.
Please contact us at email@example.com for the SDS and technical data sheets (TDS).
|Thickness||25.4 micrometers (1.1 mil)|
|Basic Weight (g/m²)||50|
|Tensile Strength - max. (MPa)||23 (MD), 28 (TD) - Method: ASTM D 882|
|Non-Std Modulus (MPa)||288 (MD), 281 (TD) - Method: ASTM D 882|
|Elongation to Break (%)||252 (MD), 311 (TD) - Method: ASTM D 882|
|Hydrogen Crossover (ml/min·cm²)||< 0.020|
|Water content (% water)||5.0 ± 3.0% - Method: ASTM D 570|
|Water uptake (% water)||50.0 ± 5.0% - Method: ASTM D 570|
|Linear Expansion % increase - 50% RH, 23°C to water soaked 23°C||10 - Method: ASTM D 570|
|Linear Expansion % increase - 50% RH, 23°C to water soaked 100°C||15 - Method: ASTM D 570|